data shee t surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v product specification ? jul 08, 2003 v.6
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 2 www.yageo.com features ? four standard sizes ? for high frequency applications ? supplied in tape on reel ? nickel-barrier end terminations. applications ? tuners ? television receivers ? video recorders ? all types of cameras ? telecommunications ? automotive ? data processing. description the capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. this structure gives rise to a high capacitance per unit volume. the inner electrodes are connected to the two terminations and finally covered with a layer of plated tin (nisn). a cross section of the structure is shown in fig.1. quick reference data description value rated voltage u r (dc) 25 v, 50 v capacitance range (e3 series): 10 nf to 470 nf tolerance on capacitance after 1000 hours 20% (m); ? 20% to + 80% (z) test voltage (dc) for 1 minute 2.5 u r sectional specifications iec 60 384-10, second edition 1989-04; also based on cecc 32 100 detailed specification based on cecc 32 101-801 climatic category (iec 60068) 10/85/21 mlb457 terminations electrodes ceramic material fig.1 construction of a cera mic multilayer capacitor.
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 3 www.yageo.com mechanical data mbb211 t l 4 l 1 l 2 l 3 w fig.2. component outline. for dimensions see table 1. physical dimensions table 1 capacitor dimensions t l 2 and l 3 case size l 1 w min. max. min. max. l 4 min. dimensions in millimetres 0603 1.6 0.10 0.8 0.07 0.73 0.87 0.25 0.65 0.40 0805 2.0 0.1 1.25 0.1 0.50 1.35 0.25 0.75 0.55 1206 3.2 0.15 1.6 0.15 0.50 1.25 0.25 0.75 1.40 1210 3.2 0.20 2.5 0.20 0.50 1.30 0.25 0.75 1.40 dimensions in inches 0603 0.063 0.004 0.032 0.003 0.029 0.035 0.010 0.026 0.016 0805 0.079 0.004 0.049 0.004 0.020 0.053 0.010 0.030 0.022 1206 0.126 0.006 0.063 0.006 0.020 0.049 0.010 0.030 0.056 1210 0.126 0.008 0.098 0.008 0.020 0.051 0.010 0.030 0.056
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 4 www.yageo.com thickness classification and packing quantities 8 mm tape width quantity per reel ? 180 mm; 7" ? 330 mm; 13" quantity per bulk case thickness classification (mm) paper blister paper blister 0603 0805 0.60 0.10 4 000 ? 20 000 ? ? 10 000 0.80 0.07 4 000 ? 15 000 ? 15 000 ? 0.50 to 1.0 ? 4 000 ? 10 000 ? ? selection chart 25 v 50 v c (nf) last two digits of 12nc 0603 0805 1206 1210 10 36 22 41 0.80 0.07 0.60 0.10 47 45 0.60 0.10 100 49 220 54 0.50 to 1.0 470 58 note 1. values in shaded cells indicate thickness class.
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 5 www.yageo.com ordering information components may be ordered by using either phycomp?s unique 12nc or a simple 15-digit clear text code. clear text code e xample : 12062e104m9b20d size code temp. char. capacitance tol. vol. termination packing marking series 0603 0805 1206 1210 2e = z5u 104=1000000 pf; the third digit signifies the number of zeros m = 20% z = ? 20%/+80% 8 = 25v 9 = 50v b = nisn 2 = 180 mm; 7" paper 3 = 330 mm; 13" paper b = 180 mm; 7" blister f = 330 mm; 13" blister p = bulk case 0 = no marking d = bme ordering code 12nc (preferred) 2 2 x x 6 2 x x 8 x x x carrier type 22 38 54 blister paper bulk size 5 0 1 2 0603 (25 v) 0805 (50 v) 1206 (50 v) 1210 (50 v) capacitance value (1) tolerance 7 8 20% ? 20% to + 80% packaging (2) 1 5 4 reel: ? 180 mm; 7" reel: ? 330 mm; 13" bulk case scm003 (1) refer to chapter ?selection chart?. (2) quantity on reel depends on thickness classification, see section ?thickness classification and packing quantities?.
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 6 www.yageo.com electrical characteristics class 2 capacitors; z5u dielectric; nisn terminations unless otherwise stated all electrical values apply at an ambient temperature of 25 1 c, an atmospheric pressure of 86 to 105 kpa, and a relative humidity of 63 to 67%. description value capacitance range (e3 se ries); note 1 25 v 50 v case size 0603 10 nf to 100 nf ? case size 0805 ? 10 nf to 100 nf case size 1206 ? 10 nf to 220 nf case size 1210 ? 100 nf 470 nf tolerance on capacitance after 1000 hours 20% (m); ? 20% / + 80% (z) tan ; note 1 4% insulation resistance after 1 minute at u r (dc) r ins > 10 g ? or r ins c > 1000 seconds, whichever is smaller maximum capacitance change with respect to capacitance at 25 c (for typical values see fig.5) + 22% to ? 56% ageing per time decade 4% 3% resistance to soldering heat 260 c; 10 seconds note 1. measured at 25 c, 0.5 v rms and 1 khz, using a four-gauge method.
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 7 www.yageo.com 0 0 ? 70 ? 50 ? 60 cca709 ? 40 ? 30 ? 10 ? 20 10 20 30 ? c c (%) v dc (v) fig.3 typical capacitance change with respect to the capacitance at 1 v as a function of dc voltage at 25 c. 0 600 0 200 100 cca710 300 500 400 20 60 80 40 100 t ( c) tan ( 10 ? 4 ) fig.4 typical tan ? 60 ? 40 ? 50 cca711 ? 30 ? 20 0 ? 10 20 60 80 40 100 ? c c (%) t ( c) fig.5 typical capa citance change as a function of tem p erature.
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 8 www.yageo.com tests and requirements table 2 test procedures and requirements iec 60384-10/ cecc 32 100 clause iec 60068-2 test method test procedure requirements 4.4 mounting the capacitors may be mounted on printed-circuit boards or ceramic substrates by applying wave soldering, reflow soldering (including vapour phase soldering) or conductive adhesive no visible damage 4.5 visual inspection and dimension check any applicable method using 10 magnification in accordance with specification 4.6.1 capacitance f = 1 khz; measuring voltage 0.5 v rms at 25 c within specified tolerance measured 1000 hours after date of manufacture 4.6.2 tan f = 1 khz; measuring voltage 0.5 v rms at 25 c in accordance with specification 4.6.3 insulation resistance at u r (dc) for 1 minute in accordance with specification 4.6.4 voltage proof 2.5 u r for one minutes max. no breakdown or flashover 4.7.1 temperature characteristic 10 to 85 c ? c/c: + 22% to ? 56% at 25 c 4.8 adhesion a force of 5 n applied for 10 s to the line joining the terminations and in a plane parallel to the substrate no visible damage mounted in accordance with cecc 32 100, paragraph 4.4 no visible damage 4.9 bond strength of plating on end face conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm ? c/c: 30%
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 9 www.yageo.com iec 60384-10/ cecc 32 100 clause iec 60068-2 test method test procedure requirements resistance to soldering heat 260 5 c for 10 0.5 s in a static solder bath the terminations shall be well tinned after recovery ? c/c: 20% tan : original specification r ins : original specification 4.10 tb resistance to leaching 260 5 c for 30 1 s in a static solder bath using visual enlargement of 10, dissolution of the terminations shall not exceed 10% 4.11 ta solderability zero hour test, and test after storage (20 to 24 months) in original packing in normal atmosphere; unmounted chips completely immersed for 2 0.5 s in a solder bath at 235 5 c the terminations shall be well tinned 4.14 ca damp heat initialization: 150 c for 1 hour, recovery 48 4 hours at 40 c; 90 to 95% rh; u r applied for 500 hours ? c/c: 30% tan : 6% max. r ins : 1000 m ? or r i c r 100 s, whichever is less 4.15 endurance initialization: 2 u r at 85 c for 1 hour (initial value) is measured after 48 4 hours; 2 u r at 85 c for 42 days, recovery 48 4 hours at room temperature after 48 hours recovery: ? c/c: 30% tan :6% max. r ins : 1000 m ? or r i c r 100 s, whichever is less
phycomp product specification surface-mount ceramic multilayer capacitors class 2, z5u 25/50 v 2003 jul 08 rev.6 10 www.yageo.com revision history revision date change notification description rev.4 2001 mar 30 - - converted to phycomp brand - capacitance range changed from e12 to e3 series. 22/02/2001 - 470 nf 12 06 no longer supported. rev.5 2003 jan 07 - - combined 25v and 50v data sheets - updated company logo rev.6 2003 jul 08 - - 1206 size 25v phase out - 0805 220nf 50v phase out - 1210 1uf 50v phase out
|